Polyurea coatings reduce marine environment’s costly effects
February 10, 2021 •Corrosion CONTROLLED, Advanced Materials
Mitigating the costly effects of maritime environments with polyurea
The marine environment, both abrasive and corrosive, is unforgiving to maritime industry structures such as offshore platforms and rigs, and ocean-going vessels—all of which are major investments for the companies operating them. The structures in a marine environment are impacted by corrosion, which costs industry billions of dollars each year for its prevention, control, and remediation.
The environment of an offshore structure can be hard on surface coatings. Some of the areas most affected are the decks, superstructure, ballast tanks, and anchor or chain wells. These are exposed to salt and other chemical agents and are susceptible to abrasion caused by the movement of people and equipment. On an oil production rig, for example, the areas where the 14-m lengths of drill pipe are laid out, dragged across the deck, and then pulled up for drilling operations, are prone to a large amount of damage. Most surface coatings are quickly abraded away, leaving bare metal that is vulnerable to corrosion.
One way to mitigate and minimize the effect of some types of corrosion is through flexible surface coatings that are resistant to chemical attack from petroleum products and salts. According to Denis Baker, special projects engineer at Rhino Linings Australasia, “a corrosion barrier has to have durability and flexibility in addition to being impermeable to the wide range of agents that affect maritime structures.” He notes it is possible to minimize some of the effects of drilling operations by applying specialized surface coatings and polyurea coatings can work to protect maritime structures in the oil and gas industry from corrosion, impact, and abrasion.
Polyurea coatings surface prep
To prepare working areas for treatment with a protective surface coating, the platform deck has to be abrasive blasted to remove any existing coatings and provide a surface profile for optimum adhesion of the primer and protective coating. Zinc-rich primers can then be applied to the prepared metal surface, over which an elastomeric polyurethane sealant/primer is rapidly sprayed. Manufacturers have developed coatings that are good choices for this type of application because they have no volatile organic component (VOC) properties and can be easily and quickly applied. For maximum protection, a pure polyurea should then be spray-applied over the primed area to a nominal thickness of 3 mm on the deck surface. This final coating is resistant to extreme weather and has excellent flexibility and high impact strength.
“Pure polyurea is a relatively modern material that has been developing rapidly during the past 15 years,” Baker says. Pure polyureas are formed when a liquid isocyanate is mixed under high pressure with an amine-driven resin solution. Isocyanates are reactive because the double covalent bond that attaches the carbon atom to nitrogen and oxygen atoms is easily broken to form single bonds in the more stable tetrahedral configuration around the carbon atom.
Application of flexible polyurea coatings
A major consideration in applying any surface treatment to a structure is the requirement to minimize downtime. Spray-coating enables quicker application and less disruption to a client's operations, and the ability to walk on a spray-applied protective surface in a matter of minutes means that a facility can be back online sooner. The beauty of pure polyurea coatings is that they are rapid setting, Baker says. They “snap cure” to form a solid surface in a few seconds and can be walked on without damage in less than a minute. “We can spray them on and they cure in as little as six seconds.” Unlike some other coatings, the pure polyurea coatings are not affected by ambient moisture or temperature while being applied, and their flexibility allows them to move with the expansion and contraction of the underlying structure as the temperature changes. Both are important considerations for an offshore coating. Another advantage is the coatings’ ability for it to be sprayed up to 6-mm thick (and greater) on a sloping or vertical surface without sagging or running. The resulting surface is easy to maintain, clean, and recoat if necessary.
Environmental considerations of applying polyurea
Where pipes and other equipment penetrate the deck areas of an offshore structure, it is important that liquids do not run down the pipes to the ocean below. Most offshore rigs cover these penetrations with a butyl rubber “boot” that is taped to the pipe and the deck. However, the rubber of the boot and the adhesive can be degraded by UV and salt exposure in a matter of months.
To extend the operational life of the deck penetration boots, a protective coating can be applied. A pure polyurea is a suitable coating material to use with the boots. When applied at a thickness of 2 mm or greater to the boot and extended 50 mm on the pipe and 100 mm onto the deck, this type of surface coating creates a liquid-tight, weather-resistant, flexible interface on all deck penetrations from 100-mm in diameter with the long-term durability.
The butyl rubber and the adjacent steel surfaces are usually scuffed and cleaned, and an appropriate primer is applied. It is important that all loose coatings, oils, and dirt are thoroughly removed before applying a new flexible membrane. Similarly, the surrounding equipment, piping, and deck surfaces must be masked off to protect against over spray.
Conclusion
Pure polyureas for spray application are typically a two-part solution that is mixed under high pressure and temperature (~20.7 MPa psi at 65 °C) in a specially designed spray apparatus. When applied, the excellent chemical cross linking produces a dense but flexible surface. The high density makes the coating almost impervious to abrasion, water, and chemicals.
AMPP has the resources to help you get the job done: Materials Performance; CoatingsPro Magazine - FREE; Maritime News - FREE.
Source: Originally appeared on coatingspromag.com and authored by Rhino Linings, Australasia.
FREE DOWNLOADS
White Paper: An Action Plan for Reducing Pipeline Failures, Costs with Corrosion in the Water Sector
Special Report: The Future of Corrosion Control, Insights from the Experts
Get Updates
Featured Articles
Categories
- 2024 Olympics (1)
- Abrasive Blasting (1)
- Advanced coating materials (9)
- Advanced Corrosion Control in Oil and Gas Industry (2)
- Advocacy (1)
- AI (2)
- Aircraft (1)
- Alkanization (1)
- AMPP (3)
- AMPP Annual Conference + Expo (1)
- Ampp Chapters (1)
- AMPP logo (1)
- Ampp Membership (1)
- Ampp Standards (1)
- Amusement parks (3)
- Architectural (1)
- Architectural Coatings (1)
- Artificial Intelligence (1)
- Asset integrity (9)
- Asset Protection (1)
- Bim Software (1)
- Biodeterioration of materials (5)
- Biofouling (4)
- Blasting (1)
- Bridges (3)
- Cathodic Protection-CP (15)
- Ceramic epoxies (1)
- Certification (1)
- Chemical Injection (1)
- Civil Engineering (1)
- Coatings (11)
- Coatings Application (1)
- Coatings failures (1)
- Coatings Industry (1)
- Coatings measurement and inspection (9)
- Coatings Systems (1)
- Concrete (12)
- Conference and Events (2)
- Corrosion (12)
- Corrosion Basics (5)
- Corrosion Control (12)
- Corrosion Control and Management (22)
- Corrosion Essentials (19)
- Corrosion Prevention (2)
- Corrosion Under Insulation (1)
- Crevice Corrosion (1)
- Cui (1)
- Data Monitoring (1)
- Department of Defense (3)
- Deposition corrosion (1)
- Dissimilar Metal Corrosion (1)
- Dissolved gases (1)
- DoD (3)
- Education (1)
- Energy industry (9)
- Epoxy (2)
- Fireproofing (1)
- Flexible coatings (2)
- Flint, Michigan (1)
- Fluoropolymer coating (3)
- Forms of Corrosion (4)
- Freshwater salinization (1)
- Galvanic (1)
- Galvanic Corrosion (3)
- General Corrosion (2)
- Hand tools (1)
- Industrial Application (3)
- Industrial Safety (1)
- Industry Best Practices (1)
- Industry Standards (1)
- Inspection (1)
- Intergranular Corrosion (1)
- Intumescent Coatings (1)
- Machine Learning (1)
- Maintenance (1)
- Maritime Coatings (11)
- Maritime industry (11)
- Master Painters Institute (1)
- Membership (2)
- Membership Benefits (2)
- Michio Kaku (1)
- Microbiological forms (1)
- Microbiologically influenced corrosion-MIC (11)
- Military (2)
- Mineral constituents (1)
- MPI (1)
- Navy (1)
- Non-Destructive Testing (1)
- Oil and Gas (1)
- Oil Fields (1)
- Organic matter (1)
- Oxgen (1)
- Paint and Protective coatings (31)
- Paint specification (1)
- Personal Protective Equipment (2)
- Petrochemical Plant Fireproofing Methods (1)
- Petrochemical Plants (1)
- Pipeline (1)
- Pitting Corrosion (2)
- Pitting Detection (1)
- Power plant (1)
- Power tools (1)
- PPE (2)
- Protective Coatings (2)
- Real-Time Corrosion Monitoring in Oil Fields (1)
- Rebar Corrosion (1)
- Reliability (1)
- Remote monitoring and drones (4)
- Repaint (1)
- Restoration (1)
- Road deicers (1)
- Roads and bridges (1)
- Roller coaster (1)
- Rust (1)
- Safety (4)
- Safety Standards (1)
- Salt pollution (1)
- Sensors (1)
- Ship Coatings (9)
- Shiptanks (1)
- Standards (9)
- Standards Committees (1)
- Steel (7)
- Steel Reinforcement (1)
- Stress Corrosion Cracking (1)
- Structural Steel (1)
- Surface Preparation (12)
- Sustainability and corrosion (7)
- Tools (1)
- Turbine (1)
- Types of Corrosion (1)
- Uniform Corrosion (1)
- Water crisis (1)
- Water pipe corrosion (1)
- Water quality (1)
- Water tank coatings (5)
- Water/treatment infrastructure (19)
- Waterway salinity (1)
- Workforce development (1)